Click here to download the instruction manual
Click here to download the settings
▌ Attention!
-
This resin is not recommended for novice users. Please download the manual before use.
-
When failed printing with RESIONE setting probably needs to change the supports settings(See more details in RESIONE instruction) or increase the normal exposure time(Printers especially mono screen will have light decay).
-
Flexible prints are easily deformed during printing, so they need thicker and denser supports.
-
If the ambient temperature is lower than 25℃, please preheat the resin liquid before printing.
-
For F39T prints with a thickness of more than 3mm, both the front and back sides need to be cured for more than 10 minutes when a post-curing box with 40W UV intensity is used. Fully post-cured prints are stronger, have a dry surface and are less likely to be scratched.
-
If the resin is not used in the 3D printer for more than 1 day, it is recommended to filter the resin with a filter funnel and pour it into an empty container. Do not pour the resin in the resin tank back to the original bottle to avoid contamination of other resins.
-
F39/F69/F39T flexible resin prints will increase in hardness as the temperature decreases.They become hard and tough prints in an environment of about 5°C, and they won’t be broken even with a hammer! If you want to keep the prints in a flexible state, it is recommended to use them in an environment above 20°C.
-
If you need a softer and faster rebound resin, please choose F80 resin.
F39T resin is a transparent flexible resin with a high printing success rate. This resin is designed to provide prints with outstanding tear strength and flexibility. It finds wide application in figure toys such as dolls' vests, capes, weapons, and footwear, tires, shoe samples, seals, buffers, gaskets, transmission belts, and various flexible prototype production. Additionally, mixing F39T with other resins can enhance the non-brittleness of printed parts.
▌ Descriptions
-
Like rubber: Flexible, tear resistance, folding resistance
-
Easy-to-use soft resin
The release agent is added to its formula, so after each exposure, the curing layer will have less adhesive force when it leaves the FEP film. In addition, the RESIONE team has specially designed the formula to ensure that the printed part exhibits a "soft with rigidity" performance during the printing process, ensuring that it does not deform.
-
As toughening agent
Mixing F69/F39/F39T resin with tough resin such as K/M58/M68/G217 can make the printed parts tougher, more durable, and not brittle for a long time.
-
Wide applications
Flexible resin is widely used in figure toys, footwear, design and industrial fields, such as tires, shoe samples, seals, gaskets, transmission belts, various flexible prototypes and dolls' vests, capes, weapons, etc.
-
Detailed print settings and user's guide
We provide settings for almost all mainstream 3D printers, and include importable settings files for different slicers, such as Chitubox/Lychee/Anycubic Workshop, etc. We also provide detailed instructions for the use of the resin and supports settings suitable for flexible resin.
▌ Certification
▌ Compatible 3D Printer
-
All series of Anycubic，Elegoo，Nova3d，Peopoly，Phrozen，Epax，Creality，Zortrax, BIQU, QIDI, UNIZ, Flashforge, Voxelab, Longer, Uniformation etc. UV 385-410nm LCD resin 3D printer
-
All series of Anycubic，Asiga, Solus series, Miicraft, Kudo3d, Flashforge，Makex，Shining etc. UV 385-410nm DLP resin 3D printer
▌ Material performance parameters
| METHOD | DATA | |
| Viscosity(25℃)(mpa.s) | ASTM:D4212-10 | 1145 |
| Liquid density(g/cm³) | ASTM:D4052-22 | 1.079 |
| Solid density(g/cm³) | ASTM:D792-20 | 1.15 |
| Shore Hardness(A) | ASTM:D2240-05 | 71 |
| Tear strength(KN/m) | ASMT:D624-98 | 17.59 |
| Tensile Strength(MPa) | ASTM: D412-06 | 6.59 |
| Tensile Modulus(MPa) | ASTM: D412-06 | 31.59 |
| Elongation at Break | ASTM: D412-06 | 222.21% |
| Water Absorption（24hr） | ASTM 570 | 1.74% |