Anti-impact resin is a robust, Nylon-like material boasting impressive impact strength and tensile toughness. Its printed objects exhibit exceptional durability, with low water absorption, high dimensional accuracy, and a wear-resistant surface that ensures long-lasting performance. With its stable mechanical properties, excellent fatigue resistance, and weather resistance, this resin is ideal for creating parts that require repeatable machining, wet or underwater operation, impact resistance, snap-on features, or even end-use products.
▌ Attention
-
Anti-impact resin liquid has the characteristic smell of acrylate, which is quite pungent. It is recommended to use it in a ventilated environment or on a 3d printer with an air purifier.
-
Anti-impact liquid viscosity is relatively high (25 ℃/77 ℉, 700mpa. s), and the stiffness of thin wall or thin diameter structure is not enough, so the printing difficulty is higher than that of standard/rigid resin. When the ambient temperature is lower than 28 ℃/82.4 ℉, it is recommended to heat the resin liquid (80 ℃/176 ℉ water bath, 5-10 minutes) before printing, and increase the "Bottom lift distance"、“lifting distance” and “rest time after retract” in the slicer.
-
Prints will become soft and weak under the following conditions: liquids are stored unsealed after long-term exposure to air (especially in the environment with high humidity); Clean with solvent or ultrasonic for more than 5 minutes. The solution when the prints becomes soft is to place them in thermostatic drying oven at 60-80 ℃ (140-176 ℉) for 30 minutes before post curing. The prints will become harder and more stable.
▌ Reviews
- The perfect resin for 3D printed action figures? --Tecco Toys (Youtube)
- 3D Print BJD Wear Resistant Joints--Helene Holz (Youtube)
▌ Descriptions
-
High impact strength and tensile toughness
-
Mechanical properties are similar to nylon and stable for a long time
-
Low water absorption, low temperature resistance, good weatherability
-
High dimensional accuracy, fine and wear-resistant surface
Anti-impact prints can meet the tolerance requirements of the outer diameter and aperture of the same printed part at the same time, with high dimensional accuracy. And the special formula makes the printing surface smooth and delicate, wear-resistant and scratch resistant.
- Special smell, and not suitable for novices
Anti-impact resin liquid has the characteristic smell of acrylate, which is quite pungent. Anti-impact liquid viscosity is relatively high (25 ℃/77 ℉, 700mpa. s), and the stiffness of thin wall or thin diameter structure is not enough, so the printing difficulty is higher than that of standard/rigid resin. When the ambient temperature is lower than 28 ℃/82.4 ℉, it is recommended to heat the resin liquid (80 ℃/176 ℉ water bath, 5-10 minutes) before printing, and increase the "Bottom lift distance"、“lifting distance” and “rest time after retract” in the slicer.
▌ Cleaning and Post-curing
- Cleaning tools: Manual cleaning or Ultrasonic cleaner or 2 in 1 Wash Cure Machine
- Cleaning time: 3mins
- Cleaning solvent: 95% Ethanol or IPA
- Post-curing light source: 385-405nm UV(40W)
- Post-curing time: 30-60mins
▌ Compatible 3D Printer
-
All series of Anycubic,Elegoo,Nova3d,Peopoly,Phrozen,Epax,Creality,Zortrax, BIQU, QIDI, UNIZ, Flashforge, Voxelab, Longer, Uniformation etc. UV 395-410nm LCD resin 3D printer
-
All series of Anycubic,Asiga, Solus series, Miicraft, Kudo3d, Flashforge,Makex,Shining etc. UV 385-410nm DLP resin 3D printer
▌ Mechanical Properties
METHOD | DATA | |
Shore Hardness | ASTM: D2240-05 | 78D |
Tensile Strength | ASTM: D638-14 | 21-28MPa |
Flexural Strength | ASTM: D790-10 | 29-37MPa |
Flexural Modulus | ASTM: D790-10 | 650-1076MPa |
Notched IZOD | ASTM: D256-10 | 46-72J/m |
Elongation at Break | ASTM: D638-14 | 81-100% |
Elongation at Yield | ASTM: D638-14 | 7.8-8.7% |
Water Absorption | ASTM: D570 | 0.46% |
Viscosity(25℃) | ASTM: D4212-10 | 715mpa.s |